焊接/高耐候钢化学成分

牌号

化学成分（质量分数）/%

C

Si

Mn

P

S

Cu

Cr

Ni

其他元素

Q265GNH

≤0.12

0.10~0.40

0.20~0.50

0.07~0.12

≤0.020

0.20~0.45

0.30~0.65

0.25~0.50^e

a,b

Q295GNH

≤0.12

0.10~0.40

0.20~0.50

0.07~0.12

≤0.020

0.25~0.45

0.30~0.65

0.25~0.50^e

a,b

Q310GNH

≤0.12

0.25~0.75

0.20~0.50

0.07~0.12

≤0.020

0.20~0.50

0.30~1.25

≤0.65

a,b

Q355GNH

≤0.12

0.25~0.75

≤0.10

0.07~0.15

≤0.020

0.25~0.55

0.30~1.25

≤0.65

a,b

Q235NH

≤0.13^f

0.10~0.40

0.20~0.60

≤0.030

≤0.030

0.25~0.55

0.40~0.80

≤0.65

a,b

Q295NH

≤0.15

0.10~0.50

0.30~1.00

≤0.030

≤0.030

0.25~0.55

0.40~0.80

≤0.65

a,b

Q355NH

≤0.16

≤0.50

0.50~1.50

≤0.030

≤0.030

0.25~0.55

0.40~0.80

≤0.65

a,b

Q415NH

≤0.12

≤0.65

≤1.10

≤0.025

≤0.030^d

0.25~0.55

0.30~1.25

0.12~0.65^e

A,b,c

Q460NH

≤0.12

≤0.65

≤1.50

≤0.025

≤0.030^d

0.25~0.55

0.30~1.25

0.12~0.65^e

A,b,c

Q500NH

≤0.12

≤0.65

≤2.00

≤0.025

≤0.030^d

0.25~0.55

0.30~1.25

0.12~0.65^e

A,b,c

Q550NH

≤0.16

≤0.65

≤2.00

≤0.025

≤0.030^d

0.25~0.55

0.30~1.25

0.12~0.65^e

A,b,c

^a为了改善钢的性能，可以添加一种或一种以上的微量合金元素：Nb 0.015％~0.060%，V0.02%～0.12%,Ti0.02%～0.10%,Ait≥0.020%。若上述元素组合使用时，应至少保证其中一种元素含量达到上述化学成分的下限规定。

^b可以添加下列合金元素：Mo≤0.30%，Zr≤0.15%。

^cNb、V、Ti等三种合金元素的添加总量不应超过0.22%。

^d供需双方协商，S的含量可以不大于0.008％。

^e供需双方商．Ni含量的下限可不做要求。

^f供需双方协商，C的含量可以不大于0.15%。